S31803/S32205

    

Introduction

Stainless steels are high-alloy steels. These steels are available in four groups that include martensitic, austenitic, ferritic and precipitation-hardened steels. These groups are formed based on the crystalline structure of stainless steels.

Stainless steels contain larger amounts of chromium in comparison with other steels and thus have good corrosion resistance. Most of the stainless steels contain about 10% of chromium.

Grade 2205 stainless steel is a duplex stainless steel whose design enables combining improved resistance to pitting, high strength, stress corrosion, crevice corrosion and cracking. Grade 2205 stainless steel resists sulfide stress corrosion and chloride environments.

The following datasheet provides an overview of grade 2205 stainless steel.

Chemical Composition

The chemical composition of grade 2205 stainless steel is outlined in the following table.

Element Content (%)
Iron, Fe 63.75-71.92
Chromium, Cr 21.0-23.0
Nickel, Ni 4.50-6.50
Molybdenum, Mo 2.50-3.50
Manganese, Mn 2.0
Silicon, Si 1.0
Nitrogen, N 0.080-0.20
Carbon, C 0.030
Phosphorous, P 0.030
Sulfur, S 0.020

Physical Properties

The following table shows the physical properties of grade 2205 stainless steel.

Properties Metric Imperial
Density 7.82 g/cm³ 0.283 lb/in³

Mechanical Properties

The mechanical properties of grade 2205 stainless steel are displayed in the following table.

Properties Metric Imperial
Tensile strength at break 621 MPa 90000 psi
Yield strength (@strain 0.200 %) 448 MPa 65000 psi
Elongation at break (in 50 mm) 25.0 % 25.0 %
Hardness, Brinell 293 293
Hardness, Rockwell c 31.0 31.0

Thermal Properties

The thermal properties of grade 2205 stainless steel are given in the following table.

Properties Metric Imperial
Thermal expansion co-efficient (@20-100°C/68-212°F) 13.7 µm/m°C 7.60 µin/in°F

Other Designations

Equivalent materials to grade 2205 stainless steel are:

  • ASTM A182 Grade F51
  • ASTM A240
  • ASTM A789
  • ASTM A790
  • DIN 1.4462

Fabrication and Heat Treatment

Annealing

Grade 2205 stainless steel is annealed at 1020-1070°C (1868-1958°F) and then water quenched.

Hot Working

Grade 2205 stainless steel is hot worked in the temperature range of 954-1149°C (1750-2100°F). Hot working of this grade stainless steel under room temperature is recommended whenever possible.

Welding

Welding methods recommended for grade 2205 stainless steel include SMAW, MIG, TIG and manual covered electrode methods. During the welding process, the material should be cooled below 149°C (300°F) between passes and preheating of the weld piece should be avoided. Low heat inputs should be used for welding grade 2205 stainless steel.

Forming

Grade 2205 stainless steel is difficult to form due to its high strength and work hardening rate.

Machinability

Grade 2205 stainless steel can be machined with either carbide or high speed tooling. The speed is reduced by about 20% when carbide tooling is used.

Applications

Grade 2205 stainless steel is used in the following applications:

  • Flue gas filters
  • Chemical tanks
  • Heat exchangers
  • Acetic acid distillation components

Stock

Form

Specification

Supply Form

Others

Sheet

Thickness?0.40-4.75mm?General Width?1000?1219?1500mm

Whole Coil or piece of it

Cold Annealed?Surface 2B?2E

Plate

Thickness?4.76-60mm?Width?1500?2000?2500mm?Length?3000?6000?8000?8500mm?Under 10mm plate can be coiled?

Whole Coil or piece of it

Single hot rolling?Solid solution annealed state?Surface 1D

Belt

Thickness?0.10-3.0mm?Width?50-500mm

Whole Coil or Specified size

Cold Annealed?Surface 2B?2E

Bar & Rod

Rolled barΦ5-45mm?Length≤1500mm

Polished Bar?circle?Square?

Solution annealing,descaling

Forged barΦ26-245mm?Length≤4000mm

Weld tube

Outer diameterΦ4.76-135mm?Wall Thickness0.25-4.00mm?Length?≤35000 mm

Base on your requirement

Use for PHE

Seamless Tube

Outer diameterΦ3-114mm?Wall Thickness0.2-4.5mm

Base on your requirement

Use for PHE

Wire

Outer diameterΦ0.1-13mm

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Forged piece

roundness and square alloy

Base on your requirement

Steel, Alloy

Flangs

All kinds of Flangs

Base on your requirement

Steel, Alloy

Welding Material

Coil wire Φ0.90mm/1.2mm/1.6mm

Base on your requirement

Certificate of Origin?America, Sweden, Britain, Germany, Austria, Italy, France.

Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm

Welding rodΦ2.4mm/3.2mm/4.0mm

Tube

Elbow, three links, four links, different diameter size

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Explosive bonded laminate

Raw Sheet Thickness≥2mm

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Tianjin Hengtai Industry & Trade Co., Ltd.
TEL:+86(0)22-82126768-618  
FAX: +86(0)22-82163689
Email: kevin.chen@timetals.com 津ICP备09000679号-1
在线客服乐语