N08800

    

Introduction

INCOLOY alloys belong to the category of super austenitic stainless steels. These alloys have nickel-chromium-iron as the base metals, with additives such as molybdenum, copper, nitrogen and silicon. These alloys are known for their excellent strength at elevated temperatures and good corrosion resistance in a variety of corrosive environments.

INCOLOY alloy 800 is an alloy of nickel, iron and chromium. The alloy is capable of remaining stable and maintaining its austenitic structure even after long time exposures to high temperatures. Other characteristics of the alloy are good strength, and high resistance to oxidizing, reducing and aqueous environments. The standard forms in which this alloy is available are round, flats, forging stock, tube, plate, sheet, wire and strip.

This datasheet will look into the chemical composition, properties and applications of INCOLOY 800.

Chemical Composition

The chemical composition of INCOLOY alloy 800 is given in the following table.

Element Content (%)
Iron, Fe ≥39.5
Nickel, Ni 30-35
Chromium, Cr 19-23
Manganese, Mn ≤1.5
Others Remainder

Physical Properties

The following table discusses the physical properties of INCOLOY alloy 800.

Properties Metric Imperial
Density 7.94 gm/cm3 0.287 lb/in3

Mechanical Properties

The mechanical properties of INCOLOY alloy 800 are tabulated below.

Properties Metric Imperial
Tensile strength(annealed) 600 MPa 87 ksi
Yield strength(annealed) 275 MPa 39.9 ksi
Elongation at Break 45% 45%

Other Designations

Some of the designations used to denote INCOLOY alloy 800 are listed below:

UNS N08800 AMS 5766 AMS 5871 ASTM B163 ASTM B366
ASTM B407 ASTM B408 ASTM B409 ASTM B514 ASTM B515
ASTM B564 DIN 1.4876      

Fabrication

Machinability

Machining characteristics of this INCOLOY alloy 800 are similar to that of iron-based alloys. This alloy tends to work-harden during machining.

Welding

INCOLOY alloy 800 can be welded by common welding techniques, using a matching filler metal.

Forming

This alloy exhibits good ductility and hence can be formed using conventional methods.

Hot working

INCOLOY alloy 800 can be hot worked at temperature ranges of 871-1232°C (1600-2250°F).

Cold Working

Cold working may be done on the alloy using standard tooling.

Annealing

INCOLOY alloy 800 may be annealed after cold working. Annealing should be done at 982°C (1800°F) for 15 min and then the alloy should be air cooled.

Applications

INCOLOY alloy 800 is used in the following applications:

  • Heat exchangers
  • Carburising equipment
  • Heating elements
  • Sheathing and nuclear steam generator tubing.

Stock

Form

Specification

Supply Form

Others

Sheet

Thickness?0.40-4.75mm?General Width?1000?1219?1500mm

Whole Coil or piece of it

Cold Annealed?Surface 2B?2E

Plate

Thickness?4.76-60mm?Width?1500?2000?2500mm?Length?3000?6000?8000?8500mm?Under 10mm plate can be coiled?

Whole Coil or piece of it

Single hot rolling?Solid solution annealed state?Surface 1D

Belt

Thickness?0.10-3.0mm?Width?50-500mm

Whole Coil or Specified size

Cold Annealed?Surface 2B?2E

Bar & Rod

Rolled barΦ5-45mm?Length≤1500mm

Polished Bar?circle?Square?

Solution annealing,descaling

Forged barΦ26-245mm?Length≤4000mm

Weld tube

Outer diameterΦ4.76-135mm?Wall Thickness0.25-4.00mm?Length?≤35000 mm

Base on your requirement

Use for PHE

Seamless Tube

Outer diameterΦ3-114mm?Wall Thickness0.2-4.5mm

Base on your requirement

Use for PHE

Wire

Outer diameterΦ0.1-13mm

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Forged piece

roundness and square alloy

Base on your requirement

Steel, Alloy

Flangs

All kinds of Flangs

Base on your requirement

Steel, Alloy

Welding Material

Coil wire Φ0.90mm/1.2mm/1.6mm

Base on your requirement

Certificate of Origin?America, Sweden, Britain, Germany, Austria, Italy, France.

Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm

Welding rodΦ2.4mm/3.2mm/4.0mm

Tube

Elbow, three links, four links, different diameter size

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Explosive bonded laminate

Raw Sheet Thickness≥2mm

Base on your requirement

Ni & Ni alloy, Ti & Ti alloy

Tianjin Hengtai Industry & Trade Co., Ltd.
TEL:+86(0)22-82126768-618  
FAX: +86(0)22-82163689
Email: kevin.chen@timetals.com 津ICP备09000679号-1
在线客服乐语